HL - Fondinox

ACI/CAST GRADE	CAST ASTM	CAST EN/DIN	CAST UNS	WROUGHT UNS	WROUGHT GRADE
HL	A297	–	–	–	–

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C	Cr	Ni	Si	Other
0.40	30.0	20.0	1.8	–

CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	Rm [MPa]	A %	Hardness [HB]	Impact [J]
240	450	10	–	–

CREEP LIMIT
Creep limit 1% 10.000 hours MPa at °C						Creep strength for 100.000 hours MPa at °C
600	700	800	900	1000	1100	600	700	800	900	1000	1100
–	58	36	19	9	–	–	46	32	17	6.5	–

PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	ρ [kg/dm³]	α [μm/m∙K] (20 – 100 °C)	K [W/m∙K]	Cp [J/kg∙K]	Melting ΔT [°C]
Austenitic, Carbides	7.72	17.8	14.2	502	1430

WORKING CONDITIONS / FABRICATION
Heat Treatment	Max working T in air [°C]	Machinability [100 = CF8M]	Patternmaker’s Shrinkage [%]
As Cast	1100	–	2.3

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
Categoria:	Fe-Cr-Ni
ACI/CAST GRADE	HL
CAST ASTM	A297
CAST EN/DIN	–
CAST UNS	–
WROUGHT UNS	–
WROUGHT GRADE	–
C	0.40
Cr	30.0
Ni	20.0
Si	1.8
Other	–
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	240
Rm [MPa]	450
A %	10
Hardness [HB]	–
Impact [J]	–
CREEP LIMIT
Creep limit 1% 10.000 hours MPa at °C
600	–
700	58
800	36
900	19
1000	9
1100	–
Creep strength for 100.000 hours MPa at °C
600	–
700	46
800	32
900	17
1000	6.5
1100	–
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	Austenitic, Carbides
ρ [kg/dm³]	7.72
α [μm/m∙K] (20 – 100 °C)	17.8
K [W/m∙K]	14.2
Cp [J/kg∙K]	502
Melting ΔT [°C]	1430
WORKING CONDITIONS / FABRICATION
Heat Treatment	As Cast
Max working T in air [°C]	1100
Machining	–
Patternmaker’s Shrinkage [%]	2.3