SANICRO 28® - Fondinox

ACI/CAST GRADE	CAST ASTM	CAST EN/DIN	CAST UNS	WROUGHT UNS	WROUGHT GRADE
–	–	1.4563 X1NiCrMoCuN31-27-4	–	N08028	SANICRO 28®

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C	Cr	Ni	Mo	Other	PREn
<0.03	27.0	31.0	3.5	1.0Cu	–

CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	Rm [MPa]	A %	Hardness [HB]	Impact [J]
200	460	30	140-200	70

PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	ρ [kg/dm³]	α [μm/m∙K] (20 – 100 °C)	K [W/m∙K]	Cp [J/kg∙K]	Melting ΔT [°C]
Austenitic	8.0	15	10	460	–

WORKING CONDITIONS / FABRICATION
Heat Treatment	Weldability	Machinability [100 = CF8M]	Patternmaker’s Shrinkage [%]
Solution Annealing	Satisfactory	–	2.8

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
Categoria:	Sandvik
ACI/CAST GRADE	–
CAST ASTM	–
CAST EN/DIN	1.4563 X1NiCrMoCuN31-27-4
CAST UNS	–
WROUGHT UNS	N08028
WROUGHT GRADE	SANICRO 28®
C	<0.03
Cr	27.0
Ni	31.0
Mo	3.5
Other	1.0Cu
PREn	–
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	200
Rm [MPa]	460
A %	30
Hardness [HB]	140-200
Impact [J]	70
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	Austenitic
ρ [kg/dm³]	8.0
α [μm/m∙K] (20 – 100 °C)	15
K [W/m∙K]	10
Cp [J/kg∙K]	460
Melting ΔT [°C]	–
WORKING CONDITIONS / FABRICATION
Heat Treatment	Solution Annealing
Weldability	Satisfactory
Machining	–
Patternmaker’s Shrinkage [%]	2.8