353MA® - Fondinox

ACI/CAST GRADE	CAST ASTM	CAST EN/DIN	CAST UNS	WROUGHT UNS	WROUGHT GRADE
–	–	1.4854 X6NiCrSiNCe35-25	–	S35315	353MA®

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C	Cr	Ni	Mo	Other	PREn
<0.20	25.0	35.0	–	Ce, N	–

CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	Rm [MPa]	A %	Hardness [HB]	Impact [J]
260	500	15	–	–

PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	ρ [kg/dm³]	α [μm/m∙K] (20 – 100 °C)	K [W/m∙K]	Cp [J/kg∙K]	Melting ΔT [°C]
Austenitic, Carbides	7.9	–	–	–	–

WORKING CONDITIONS / FABRICATION
Heat Treatment	Weldability	Machinability [100 = CF8M]	Patternmaker’s Shrinkage [%]
As Cast	–	–	2.6

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
Categoria:	Outokumpu Oy
ACI/CAST GRADE	–
CAST ASTM	–
CAST EN/DIN	1.4854 X6NiCrSiNCe35-25
CAST UNS	–
WROUGHT UNS	S35315
WROUGHT GRADE	353MA®
C	<0.20
Cr	25.0
Ni	35.0
Mo	–
Other	Ce, N
PREn	–
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	260
Rm [MPa]	500
A %	15
Hardness [HB]	–
Impact [J]	–
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	Austenitic, Carbides
ρ [kg/dm³]	7.9
α [μm/m∙K] (20 – 100 °C)	–
K [W/m∙K]	–
Cp [J/kg∙K]	–
Melting ΔT [°C]	–
WORKING CONDITIONS / FABRICATION
Heat Treatment	As Cast
Weldability	–
Machining	–
Patternmaker’s Shrinkage [%]	2.6