1.4729 - Fondinox

ACI/CAST GRADE	CAST ASTM	CAST EN/DIN	CAST UNS	WROUGHT UNS	WROUGHT GRADE
CA40	A743	1.4729 GX40CrSi13	J91553	–	–

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C	Cr	Ni	Si	Other
0.38	13.0	–	1.8	–

CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	Rm [MPa]	A %	Hardness [HB]	Impact [J]
–	–	–	–	–

CREEP LIMIT
Creep limit 1% 10.000 hours MPa at °C						Creep strength for 100.000 hours MPa at °C
600	700	800	900	1000	1100	600	700	800	900	1000	1100
22	9	3.5	1	–	–		–	–	–	–	–

PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	ρ [kg/dm³]	α [μm/m∙K] (20 – 100 °C)	K [W/m∙K]	Cp [J/kg∙K]	Melting ΔT [°C]
Ferrite, Carbides	–	–	–	–	–

WORKING CONDITIONS / FABRICATION
Heat Treatment	Max working T in air [°C]	Machinability [100 = CF8M]	Patternmaker’s Shrinkage [%]
As Cast	850		2

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
Categoria:	Fe-Cr
ACI/CAST GRADE	CA40
CAST ASTM	A743
CAST EN/DIN	1.4729 GX40CrSi13
CAST UNS	J91553
WROUGHT UNS	–
WROUGHT GRADE	–
C	0.38
Cr	13.0
Ni	–
Si	1.8
Other	–
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	–
Rm [MPa]	–
A %	–
Hardness [HB]	–
Impact [J]	–
CREEP LIMIT
Creep limit 1% 10.000 hours MPa at °C
600	22
700	9
800	3.5
900	1
1000	–
1100	–
Creep strength for 100.000 hours MPa at °C
600
700	–
800	–
900	–
1000	–
1100	–
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	Ferrite, Carbides
ρ [kg/dm³]	–
α [μm/m∙K] (20 – 100 °C)	–
K [W/m∙K]	–
Cp [J/kg∙K]	–
Melting ΔT [°C]	–
WORKING CONDITIONS / FABRICATION
Heat Treatment	As Cast
Max working T in air [°C]	850
Machining
Patternmaker’s Shrinkage [%]	2