HD - Fondinox

ACI/CAST GRADE	CAST ASTM	CAST EN/DIN	CAST UNS	WROUGHT UNS	WROUGHT GRADE
HD	A297	1.4823 GX40CrNiSi27-4	J93005	–	–

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C	Cr	Ni	Si	Other
0.42	26.5	4.5	1.8	–

CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	Rm [MPa]	A %	Hardness [HB]	Impact [J]
240	515	8	–	–

CREEP LIMIT
Creep limit 1% 10.000 hours MPa at °C						Creep strength for 100.000 hours MPa at °C
600	700	800	900	1000	1100	600	700	800	900	1000	1100

PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	ρ [kg/dm³]	α [μm/m∙K] (20 – 100 °C)	K [W/m∙K]	Cp [J/kg∙K]	Melting ΔT [°C]
Ferrite, Austenite, Carbides	7.58	11	22	500	1430 (L)

WORKING CONDITIONS / FABRICATION
Heat Treatment	Max working T in air [°C]	Machinability [100 = CF8M]	Patternmaker’s Shrinkage [%]
As Cast	1050		2

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
Categoria:	Fe-Cr-Ni
ACI/CAST GRADE	HD
CAST ASTM	A297
CAST EN/DIN	1.4823 GX40CrNiSi27-4
CAST UNS	J93005
WROUGHT UNS	–
WROUGHT GRADE	–
C	0.42
Cr	26.5
Ni	4.5
Si	1.8
Other	–
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	240
Rm [MPa]	515
A %	8
Hardness [HB]	–
Impact [J]	–
CREEP LIMIT
Creep limit 1% 10.000 hours MPa at °C
600
700
800
900
1000
1100
Creep strength for 100.000 hours MPa at °C
600
700
800
900
1000
1100
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	Ferrite, Austenite, Carbides
ρ [kg/dm³]	7.58
α [μm/m∙K] (20 – 100 °C)	11
K [W/m∙K]	22
Cp [J/kg∙K]	500
Melting ΔT [°C]	1430 (L)
WORKING CONDITIONS / FABRICATION
Heat Treatment	As Cast
Max working T in air [°C]	1050
Machining
Patternmaker’s Shrinkage [%]	2