M35-2 - Fondinox

ACI/CAST GRADE	CAST ASTM	CAST EN/DIN	CAST UNS	WROUGHT UNS	WROUGHT GRADE
M35-2	A494	–	N24020	–	–

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C	Cr	Ni	Mo	Other	PREn
<0.35	–	Bal.	–	29.0Cu, Fe<3.5, Nb<0.5	–

CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	Rm [MPa]	A %	Hardness [HB]	Impact [J]
205	450	25	140-200	70

PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	ρ [kg/dm³]	α [μm/m∙K] (20 – 100 °C)	K [W/m∙K]	Cp [J/kg∙K]	Melting ΔT [°C]
Austenitic	8.63	–	–	–	–

WORKING CONDITIONS / FABRICATION
Heat Treatment	Weldability	Machinability [100 = CF8M]	Patternmaker’s Shrinkage [%]
Annealing	Excellent	–	1.8

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
Categoria:	Nickel Base
ACI/CAST GRADE	M35-2
CAST ASTM	A494
CAST EN/DIN	–
CAST UNS	N24020
WROUGHT UNS	–
WROUGHT GRADE	–
C	<0.35
Cr	–
Ni	Bal.
Mo	–
Other	29.0Cu, Fe<3.5, Nb<0.5
PREn	–
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	205
Rm [MPa]	450
A %	25
Hardness [HB]	140-200
Impact [J]	70
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	Austenitic
ρ [kg/dm³]	8.63
α [μm/m∙K] (20 – 100 °C)	–
K [W/m∙K]	–
Cp [J/kg∙K]	–
Melting ΔT [°C]	–
WORKING CONDITIONS / FABRICATION
Heat Treatment	Annealing
Weldability	Excellent
Machining	–
Patternmaker’s Shrinkage [%]	1.8