CG6MMN - Fondinox

ACI/CAST GRADE	CAST ASTM	CAST EN/DIN	CAST UNS	WROUGHT UNS	WROUGHT GRADE
CG6MMN	A351, A743	–	J93790	S20910	NITRONIC 50®

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C	Cr	Ni	Mo	Other	PREn
<0.06	22.0	12.5	2.0	5.0Mn, 0.3N, 0.2V, 0.2Nb

CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	Rm [MPa]	A %	Hardness [HB]	Impact [J]
295	585	30	150-220	120

PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	ρ [kg/dm³]	α [μm/m∙K] (20 – 100 °C)	K [W/m∙K]	Cp [J/kg∙K]	Melting ΔT [°C]
Austenitic	7.75	16	–	–	1415-1450

WORKING CONDITIONS / FABRICATION
Heat Treatment	Weldability	Machinability [100 = CF8M]	Patternmaker’s Shrinkage [%]
Solution Annealing	Satisfactory	91	2.6

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
Categoria:	Austenitic
ACI/CAST GRADE	CG6MMN
CAST ASTM	A351, A743
CAST EN/DIN	–
CAST UNS	J93790
WROUGHT UNS	S20910
WROUGHT GRADE	NITRONIC 50®
C	<0.06
Cr	22.0
Ni	12.5
Mo	2.0
Other	5.0Mn, 0.3N, 0.2V, 0.2Nb
PREn
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	295
Rm [MPa]	585
A %	30
Hardness [HB]	150-220
Impact [J]	120
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	Austenitic
ρ [kg/dm³]	7.75
α [μm/m∙K] (20 – 100 °C)	16
K [W/m∙K]	–
Cp [J/kg∙K]	–
Melting ΔT [°C]	1415-1450
WORKING CONDITIONS / FABRICATION
Heat Treatment	Solution Annealing
Weldability	Satisfactory
Machining	91
Patternmaker’s Shrinkage [%]	2.6