HASTELLOY C2000®

ACI/CAST GRADE	CAST ASTM	CAST EN/DIN	CAST UNS	WROUGHT UNS	WROUGHT GRADE
–	–	2.4675	–	N06200	HASTELLLOY C2000®

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C	Cr	Ni	Mo	Other	PREn
<0.02	23.0	Bal.	16.0	Fe<3.0, 1.6Cu	–

CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	Rm [MPa]	A %	Hardness [HB]	Impact [J]
275	550	25	160-230	100

PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	ρ [kg/dm³]	α [μm/m∙K] (20 – 100 °C)	K [W/m∙K]	Cp [J/kg∙K]	Melting ΔT [°C]
Austenitic, (Intermetallics)	8.5	12.4	9.1	428	1328-1358

WORKING CONDITIONS / FABRICATION
Heat Treatment	Weldability	Machinability [100 = CF8M]	Patternmaker’s Shrinkage [%]
Solution Annealing	Excellent	–	1.8

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
Categoria:	Haynes Intl.
ACI/CAST GRADE	–
CAST ASTM	–
CAST EN/DIN	2.4675
CAST UNS	–
WROUGHT UNS	N06200
WROUGHT GRADE	HASTELLLOY C2000®
C	<0.02
Cr	23.0
Ni	Bal.
Mo	16.0
Other	Fe<3.0, 1.6Cu
PREn	–
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	275
Rm [MPa]	550
A %	25
Hardness [HB]	160-230
Impact [J]	100
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	Austenitic, (Intermetallics)
ρ [kg/dm³]	8.5
α [μm/m∙K] (20 – 100 °C)	12.4
K [W/m∙K]	9.1
Cp [J/kg∙K]	428
Melting ΔT [°C]	1328-1358
WORKING CONDITIONS / FABRICATION
Heat Treatment	Solution Annealing
Weldability	Excellent
Machining	–
Patternmaker’s Shrinkage [%]	1.8