WORKING CONDITIONS / FABRICATION | |||
---|---|---|---|
Heat Treatment | Weldability | Machinability [100 = CF8M] | Patternmaker’s Shrinkage [%] |
Solution Annealing | Excellent | – | 1.8 |
Categoria: | Haynes Intl. | ||||
---|---|---|---|---|---|
ACI/CAST GRADE |
– | ||||
CAST ASTM | – | ||||
CAST EN/DIN | 2.4675 | ||||
CAST UNS | – | ||||
WROUGHT UNS |
N06200 | ||||
WROUGHT GRADE |
HASTELLLOY C2000® | ||||
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES) | |||||
C | <0.02 | ||||
Cr | 23.0 | ||||
Ni | Bal. | ||||
Mo | 16.0 | ||||
Other | Fe<3.0, 1.6Cu | ||||
PREn | – | ||||
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED) | |||||
Rp0.2[MPa] | 275 | ||||
Rm [MPa] | 550 | ||||
A % | 25 | ||||
Hardness [HB] | 160-230 | ||||
Impact [J] | 100 | ||||
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED) | |||||
Microstructure | Austenitic, (Intermetallics) | ||||
ρ [kg/dm3] | 8.5 | ||||
α [μm/m∙K] (20 – 100 °C) | 12.4 | ||||
K [W/m∙K] | 9.1 | ||||
Cp [J/kg∙K] | 428 | ||||
Melting ΔT [°C] | 1328-1358 | ||||
WORKING CONDITIONS / FABRICATION | |||||
Heat Treatment | Solution Annealing | ||||
Weldability | Excellent | ||||
Machining | – | ||||
Patternmaker’s Shrinkage [%] | 1.8 |