1.4500 - Fondinox

ACI/CAST GRADE	CAST ASTM	CAST EN/DIN	CAST UNS	WROUGHT UNS	WROUGHT GRADE
–	–	1.4500 GX7NiCrMoCuNb25-20	–	–	–

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C	Cr	Ni	Mo	Other	PREn
<0.08	20.0	25.0	3.0	2.0Cu, Nb>8x%C	–

CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	Rm [MPa]	A %	Hardness [HB]	Impact [J]
185	440	20	130-200	50

PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	ρ [kg/dm³]	α [μm/m∙K] (20 – 100 °C)	K [W/m∙K]	Cp [J/kg∙K]	Melting ΔT [°C]
Austenitic	7.9	–	–	–	–

WORKING CONDITIONS / FABRICATION
Heat Treatment	Weldability	Machinability [100 = CF8M]	Patternmaker’s Shrinkage [%]
Solution Annealing	Satisfactory		2.6

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
Categoria:	Superaustenitic
ACI/CAST GRADE	–
CAST ASTM	–
CAST EN/DIN	1.4500 GX7NiCrMoCuNb25-20
CAST UNS	–
WROUGHT UNS	–
WROUGHT GRADE	–
C	<0.08
Cr	20.0
Ni	25.0
Mo	3.0
Other	2.0Cu, Nb>8x%C
PREn	–
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	185
Rm [MPa]	440
A %	20
Hardness [HB]	130-200
Impact [J]	50
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	Austenitic
ρ [kg/dm³]	7.9
α [μm/m∙K] (20 – 100 °C)	–
K [W/m∙K]	–
Cp [J/kg∙K]	–
Melting ΔT [°C]	–
WORKING CONDITIONS / FABRICATION
Heat Treatment	Solution Annealing
Weldability	Satisfactory
Machining
Patternmaker’s Shrinkage [%]	2.6