ACI/CAST
GRADE
CAST ASTM CAST EN/DIN CAST UNS WROUGHT
UNS
WROUGHT
GRADE
CF3MS 1.4435 X2CrNiMo18-14-3 AISI 316LS
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C Cr Ni Mo Other PREn
<0.03 19.0 13.5 2.7
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] Rm [MPa] A % Hardness [HB] Impact [J]
205 485 25 140-200 120
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure ρ [kg/dm3] α [μm/m∙K] (20 – 100 °C) K [W/m∙K] Cp [J/kg∙K] Melting ΔT [°C]
Austenitic 7.75
WORKING CONDITIONS / FABRICATION
Heat Treatment Weldability Machinability [100 = CF8M] Patternmaker’s Shrinkage [%]
Solution Annealing Excellent 100 2.6
Categoria: Austenitic
ACI/CAST
GRADE
CF3MS
CAST ASTM
CAST EN/DIN 1.4435 X2CrNiMo18-14-3
CAST UNS
WROUGHT
UNS
WROUGHT
GRADE
AISI 316LS
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C <0.03
Cr 19.0
Ni 13.5
Mo 2.7
Other
PREn
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp0.2[MPa] 205
Rm [MPa] 485
A % 25
Hardness [HB] 140-200
Impact [J] 120
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure Austenitic
ρ [kg/dm3] 7.75
α [μm/m∙K] (20 – 100 °C)
K [W/m∙K]
Cp [J/kg∙K]
Melting ΔT [°C]
WORKING CONDITIONS / FABRICATION
Heat Treatment Solution Annealing
Weldability Excellent
Machining 100
Patternmaker’s Shrinkage [%] 2.6