UMCO50 - Fondinox

ACI/CAST GRADE	CAST ASTM	CAST EN/DIN	CAST UNS	WROUGHT UNS	WROUGHT GRADE
UMCO50	–	2.4778 GCoCr28	–	–	–

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C	Cr	Ni	Si	Other
0.09	28.0	–	1.0	49.5Co

CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	Rm [MPa]	A %	Hardness [HB]	Impact [J]
–	500	6	–	–

CREEP LIMIT
Creep limit 1% 10.000 hours MPa at °C						Creep strength for 100.000 hours MPa at °C
600	700	800	900	1000	1100	600	700	800	900	1000	1100
–	60	35	21	8	3.5	–	55	28	19	4	–

PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	ρ [kg/dm³]	α [μm/m∙K] (20 – 100 °C)	K [W/m∙K]	Cp [J/kg∙K]	Melting ΔT [°C]
Austenitic, Carbides	8.05	–	–	–	–

WORKING CONDITIONS / FABRICATION
Heat Treatment	Max working T in air [°C]	Machinability [100 = CF8M]	Patternmaker’s Shrinkage [%]
As Cast	1150	–	2.5

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
Categoria:	Nickel and Cobalt Base
ACI/CAST GRADE	UMCO50
CAST ASTM	–
CAST EN/DIN	2.4778 GCoCr28
CAST UNS	–
WROUGHT UNS	–
WROUGHT GRADE	–
C	0.09
Cr	28.0
Ni	–
Si	1.0
Other	49.5Co
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	–
Rm [MPa]	500
A %	6
Hardness [HB]	–
Impact [J]	–
CREEP LIMIT
Creep limit 1% 10.000 hours MPa at °C
600	–
700	60
800	35
900	21
1000	8
1100	3.5
Creep strength for 100.000 hours MPa at °C
600	–
700	55
800	28
900	19
1000	4
1100	–
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	Austenitic, Carbides
ρ [kg/dm³]	8.05
α [μm/m∙K] (20 – 100 °C)	–
K [W/m∙K]	–
Cp [J/kg∙K]	–
Melting ΔT [°C]	–
WORKING CONDITIONS / FABRICATION
Heat Treatment	As Cast
Max working T in air [°C]	1150
Machining	–
Patternmaker’s Shrinkage [%]	2.5