CF3MS - Fondinox

ACI/CAST GRADE	CAST ASTM	CAST EN/DIN	CAST UNS	WROUGHT UNS	WROUGHT GRADE
CF3MS	–	1.4435 X2CrNiMo18-14-3	–	–	AISI 316LS

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
C	Cr	Ni	Mo	Other	PREn
<0.03	19.0	13.5	2.7	–

CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	Rm [MPa]	A %	Hardness [HB]	Impact [J]
205	485	25	140-200	120

PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	ρ [kg/dm³]	α [μm/m∙K] (20 – 100 °C)	K [W/m∙K]	Cp [J/kg∙K]	Melting ΔT [°C]
Austenitic	7.75	–	–	–	–

WORKING CONDITIONS / FABRICATION
Heat Treatment	Weldability	Machinability [100 = CF8M]	Patternmaker’s Shrinkage [%]
Solution Annealing	Excellent	100	2.6

CHEMICAL COMPOSITION (wt%, TYPICAL VALUES)
Categoria:	Austenitic
ACI/CAST GRADE	CF3MS
CAST ASTM	–
CAST EN/DIN	1.4435 X2CrNiMo18-14-3
CAST UNS	–
WROUGHT UNS	–
WROUGHT GRADE	AISI 316LS
C	<0.03
Cr	19.0
Ni	13.5
Mo	2.7
Other	–
PREn
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Rp_0.2[MPa]	205
Rm [MPa]	485
A %	25
Hardness [HB]	140-200
Impact [J]	120
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED)
Microstructure	Austenitic
ρ [kg/dm³]	7.75
α [μm/m∙K] (20 – 100 °C)	–
K [W/m∙K]	–
Cp [J/kg∙K]	–
Melting ΔT [°C]	–
WORKING CONDITIONS / FABRICATION
Heat Treatment	Solution Annealing
Weldability	Excellent
Machining	100
Patternmaker’s Shrinkage [%]	2.6