ACI/CAST GRADE |
CAST ASTM | CAST EN/DIN | CAST UNS | WROUGHT UNS |
WROUGHT GRADE |
---|---|---|---|---|---|
HR-235® Alloy | – | – | – | N06235 | – |
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES) | |||||
---|---|---|---|---|---|
C | Cr | Ni | Mo | Other | PREn |
<0.06 | 31.0 | Bal. | 5.6 | 3.8 Cu |
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED) | |||||
---|---|---|---|---|---|
Rp0.2[MPa] | Rm [MPa] | A % | Hardness [HB] | Impact [J] | |
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED) | |||||
---|---|---|---|---|---|
Microstructure | ρ [kg/dm3] | α [μm/m∙K] (20 – 100 °C) | K [W/m∙K] | Cp [J/kg∙K] | Melting ΔT [°C] |
WORKING CONDITIONS / FABRICATION | |||
---|---|---|---|
Heat Treatment | Weldability | Machinability [100 = CF8M] | Patternmaker’s Shrinkage [%] |
Solution Annealing | Excellent |
Categoria: | Haynes Intl. | ||||
---|---|---|---|---|---|
ACI/CAST GRADE |
HR-235® Alloy | ||||
CAST ASTM | – | ||||
CAST EN/DIN | – | ||||
CAST UNS | – | ||||
WROUGHT UNS |
N06235 | ||||
WROUGHT GRADE |
– | ||||
CHEMICAL COMPOSITION (wt%, TYPICAL VALUES) | |||||
C | <0.06 | ||||
Cr | 31.0 | ||||
Ni | Bal. | ||||
Mo | 5.6 | ||||
Other | 3.8 Cu | ||||
PREn | |||||
CASTINGS MINIMUM MECHANICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED) | |||||
Rp0.2[MPa] | |||||
Rm [MPa] | |||||
A % | |||||
Hardness [HB] | |||||
Impact [J] | |||||
PHYSICAL PROPERTIES (AT 20°C, UNLESS OTHERWISE SPECIFIED) | |||||
Microstructure | |||||
ρ [kg/dm3] | |||||
α [μm/m∙K] (20 – 100 °C) | |||||
K [W/m∙K] | |||||
Cp [J/kg∙K] | |||||
Melting ΔT [°C] | |||||
WORKING CONDITIONS / FABRICATION | |||||
Heat Treatment | Solution Annealing | ||||
Weldability | Excellent | ||||
Machining | |||||
Patternmaker’s Shrinkage [%] |